Vinyl Acetate - Ethylene Emulsion Polymers (VAE)
Specification of VAE Emulsions
Grade
Polymer Type
Solid
Content*
wt%
Viscosity*
cP
25°C, 60rpm
pH*
Free
Monomer*
wt%
Protective
Colloid
Ionic
Type
Tg on
set, °C
TDS
MSDS
Vinyl-Acetate Ethylene Copolymer Emulsions (VAE)
DA-100L
 VAE
 54.5min
 500~1000
 4.5~6.5
 0.1max
 PVA
 nonionic
 0
X
  
DA-100
 VAE
 55±1
 1100~1600
 4.5~6.5
 0.5max
 PVA
 nonionic
 0
X
  
DA-101
 VAE
 55min
 1500~2500
 4.5~6.5
 0.5max
 PVA
 nonionic
 0
X
X
DA-102
 VAE
 55min
 2500~3700
 4.5~6.5
 0.5max
 PVA
 nonionic
 0
X
X
DA-102H
 VAE
 55min
 3500~4500
 4.5~6.5
 0.5max
 PVA
 nonionic
 0
X
  
DA-103
 VAE
 60min
 1500~2500
 4.5~6.5
 0.5max
 PVA
 nonionic
 0
X
  
DA-103H
 VAE
 60min
 3200~4200
 4.5~6.5
 0.5max
 PVA
 nonionic
 0
X
  
DA-104
 VAE
 55min
 2000~3000
 4.5~6.5
 0.5max
 PVA
 nonionic
 -15±5*
X
X
DA-107
 VAE
 65min
 1500~2500
 4.5~6.5
 1.0max
 PVA
 nonionic
 0
X
  
DA-108H
 VAE
 72min
 2500~5000
 4.5~6.5
 1.0max
 PVA
 nonionic
 0
X
  
DA-111
 VAE
 55min
 1500~2500
 4.5~6.5
 0.5max
 PVA
 nonionic
 15±3*
X
  
DA-125
 VAE
 55min
 2500-3500
 4.5~6.5
 0.5max
 PVA
 nonionic
 -8±4*
 X
  
DA-128
 VAE
 60±1
 5000~7500
 4.5~6.5
 0.5max
 PVA
 nonionic
 -13±3*
X
  
TP-134N
VAE
 55±1
 100~500
 4.5~6.5
 0.1max
PVA
nonionic
.0±3*
X
X
DA-181
 VAE
 55min
 1500~2500
 4.5~6.5
 0.5max
 PVA
 nonionic
 0
X
  
DA-183
 VAE
 55min
 1500~2500
 4.5~6.5
 0.5max
 PVA
 nonionic
 0
X
  
DA-265
 VAE-Acrylate
 65min
 1000~2000
 4.5~6.5
 1.0max
 Cellulose
 anionic
 -25±5*
X
  
DA-265H
 VAE-Acrylate
 65min
 2000~3000
 4.5~6.5
 1.0max
 Cellulose
 anionic
 -25±5*
 
  
DA-310
 Carboxylated VAE
 60min
 1000~2000
 3.5~5.5
 1.0max
 PVA
 anionic
 0
X
  
DA-371
VAE-Silane
53min
500~1500
4.5~6.5
0.1max
PVA
nonionic
10±3*
X
X
DA-500
 VAE
 54.5min
 500~1000
 4.5~6.5
 0.5max
 PVA
 nonionic
 0
 
  
DA-501
 VAE
 54.5min
 1000~1500
 4.5~6.5
 0.5max
 PVA
 nonionic
 0
 
  
DA-502
 VAE
 54.5min
 3000~4000
 4.5~6.5
 0.5max
 PVA
 nonionic
 0
X
  
DA-511
 VAE
 55min
 1500~2500
 4.5~6.5
 0.5max
 PVA
 nonionic
 15±3*
X
  
DA-523
 VAE
 55min
 700~1000
 4.5~6.5
 0.5max
 PVA
 nonionic
 20±3*
X
  
DA-524
 VAE
 55min
 1500~2500
 4.5~6.5
 0.5max
 PVA
 nonionic
 20±3*
X
  
DA-532
 VAE
 55min
 1800~2700
 4.5~6.5
 0.5max
 PVA
 nonionic
 10±3*
X
  
DA-652
 VAE
 54~57
 15000-20000▲1
 4.0~7.0
 0.5max
 PVA
 nonionic
 0
X
  
DA-691
 VAE
 54.5min
 100~500
 5.0~7.5
 0.5max
 PVA
 nonionic
 0
 
  
DA-845
 VAE
 45±1
 1000±200▲2
 4.5~6.5
 -
 PVA
 nonionic
 0
 
  
DA-855
 VAE
 55±1
 1700±300▲2
 5.0~6.5
 -
 PVA
 nonionic
 0
 
  
* The above specification is subject to change without any notice
▲1:25°C.30rpm   ▲2:30°C.10rpm

For Adobe Acrobat reader click here
Vinyl Acetate-Ethylene Emulsion is a copolymer of vinyl acetate with low ethylene content
having been developed as a powerful adhesive base, which offers the following special
characteristics :

Initial Adhesive
Strength High Wet Tack,
Good Creep Resistance
Water Resistance
Alkali Resistance
Good Thickening Response
Operation Safety

VAE Emulsion can bond a greater variety of surface than presently available polyvinyl acetate
emulsion base, and particularly effective in bonding polyvinyl chloride films. The VAE emulsion
effectively bonds such widely variety substrate as paper, wood, cotton cloth, hardboard,
urethane foam and certain types of coated paperboard.  Vinyl Acetate-Ethylene Emulsion
(VAE Emulsion) also effectively uses for civil and construction works to improve the adhesive
power and water resistance of mortar.